A new curing agent was synthesized by the reaction of phenylamine-formaldehyde and dicyanodiamide.

利用苯胺-甲醛与双氰胺反应得到了一种改性产物。

The effects of isocyano-content, the amount of catalyst and the proportion of resin to curing agent on the product properties were discussed.

讨论了异氰酸根含量、催化剂用量,以及树脂和固化剂配比对产品性能的影响。

The influences of the arylated alkyl amine and conventional polyamide curing agent on the performance of light epoxy antistatic coatings were studied respectively.

使用导电云母粉研制浅色环氧防静电涂料,不仅导电粉的选择至关重要,环氧固化剂的选择也非常关键。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。